It is a highly compatible repair material for repairing broken and cracked parts of all aluminum engine blocks, machine bodies, completing parts, filling shaft bearings and casting cavities.
After hardening, ALCON F is resistant to fuels, water, oil, vibration and a certain degree of heat.
| Product Code | Color | Packaging Type | Pieces |
| M-2224 | Aluminium | 500 gr. Box | 10 |
Color: After mixing Aluminum
Mixture ratio; Weight: 9;1-Volume: 4;1
Curing at 23° C for 500 g: 60 minutes
Maximum working heat: 121°C
Spesific volume: 628 cm³/kg
Heat Resistance: [- 35 °C / + 120 °C]
Preparation of the bonding material:
The surface should be cleaned from water, oil, rust and dirt. If the surface is glossy. The surface should be roughened with sandpaper and file.
Application:
Given in two components of ALCON F metal bond;
Aluminium colored resin as volume 4 scales (as weight 9 units) White colored hardener as volume 1 scale(as weight 1 unit). Thoroughly mixed, spread on both sides of the bonding parts and compound carefully. Wait until ıt becomes harden.
Hardening:
At room temperature 25-30°C, takes 4-6 hours. If you are prompted early hardening pasted parts in a flameless heating at 70-90°C, the desired result can be achieved in 2-3 hours.
It is used to repair for all aluminium engine blocks,cracks and fracture zones of machine, completion parts of machine. It is a very compatible material to fill nad repair for the gaps of shaft bearings and cast.
Keep under lock and key and out of reach of children.
Avoid contact with skin
Rinse immediately with plenty of water and seek contact with eyes.
After contact with skin wash immediately with soap and water.
Suitable protective clothing, gloves and eye / face protection.
Consult a doctor immediately in case of accident or if you feel unwell.
Avoid release to the environment.